Remove oil, grease and other chemical contaminants by solvent wipe or steam cleaning. Because of the lack of “standards” for minimal surface preparation, test applications should be made to determine adequate surface cleanliness and compatibility with existing paint. The surface should be dry and at least 5☏ above the dew point.īest method is a near white abrasive blast (SSPC-SP10) but E517M will perform well over minimally prepare surfaces depending on service requirements. When spraying, use a 50% overlapping crosshatch pattern to minimize the occurrence of pinholes. For maximum exterior gloss and color retention apply a topcoat of CT-370 polyurethane. Heaters that emit carbon dioxide and carbon monoxide can cause the coating to yellow. ![]() This will affect the color but will have no effect on the performance of the product. Low temperature cure hardener colors will be a little darker than the regular cure. Epoxy coatings may yellow or darken during application and after final cure. Be sure the batch numbers are all the same to provide uniform color. For safety and proper product curing, good ventilation is necessary when painting indoors or in confined areas. Times may be longer for thickness above 5 dry mils. Up to 20% S-74 mixed per gallon or substitute 100% MEK Method: ASTM D522, 180º Bend Result: Passes 7/8”Īpplication Temp (curing temp down to 40F for regular cure and 25F for Low Temp cureĬS 17 Wheel, 1000 cycles, 1000 g Load Result: ave 10 mg ASTM D4060 Mix 4 parts Base (Part A) to 1 part Hardener (Part B) per gallonġ gallon 5 gallon (5 gallon ships LTL Freight only)Ĥ:1 by volume. Recommended Coverage & Dry Film Thicknessĥ.0 – 12.0 dry mils at 125-295 sq. Vertical surfaces up to 15 mils one coat.Excellent flexibility passes 7/8″ conical mandrel 180º Bend.Outstanding impact and abrasion resistance.Excellent chemical resistance to acids, caustics, solvents.Performs well over epoxy mortars and properly primed concrete surfaces.Excellent as a secondary containment coating.Excellent as a primary containment coating for internal tank linings (when part of specified system).Sewage and waste water treatment facilities.TOPCOAT: Recommend CT-370 for exterior applications for color retention and gloss When using E517M as primary chemical containment, recommend E15M Epoxy Primer PRIMER: Recommend a concrete primer when applying E517M over concrete. ![]() Available in a regular cure and fast set low temp cure to 25☏. 5 Gallon kits available special order only, minimum order 40 gallons LTL Freight to commercial location only). Fast Cure formula available for cold weather applying to surfaces down to 38° (needs to remain at this temp or above for at least 1 hour) and then during curing process temperatures further dropping ok to as low as 25☏.Įasy to apply with brush, roll and airless and conventional spray.Īvailable in wide range of 6 colors in 1 gallon kits. Regular cure Low Temperature application down to 45☏ (air and surface low temperature during curing process). Great for primary containment and tank linings for wide range of chemicals when chemical contact temperatures below 150☏ and used with E15M Epoxy Mastic Primer as part of a specified system (contact us with chemical exposure requirements for system details at For primary containment and tank lining projects to protect against even more aggressive chemicals, see our E1500VN Novolac Epoxy. The E517M has excellent chemical resistance to a wide range of of acids, caustics and many solvents for spill, splash and short term immersion (up to 72 hours) as a secondary containment coating. The E517M unique coating has excellent chemical, abrasion, impact, and weather resistance with outstanding adhesion to marginally prepared surfaces as well as clean blasted steel surfaces. E517M Epoxy can be used on steel and concrete as a one coat, 20 mil dry film Epoxy on horizontal surfaces and up to 15 mils on vertical surfaces in one coat. ![]() E517M is based on a cycloaliphatic polyamine cured Epoxy. E517M is a high performance two component, high solids, high build, flake filled, Phenolic Epoxy Mastic.
0 Comments
Leave a Reply. |
AuthorWrite something about yourself. No need to be fancy, just an overview. ArchivesCategories |